铝合金 7075 板材信息

网站首页    铝合金    铝合金 7075 板材信息

img1Sheet Coil & Plate Alloy 7075

Technical Data

 

ALLOY DESCRIPTION

The superior stress corrosion resistance of the Tl 73 and T735 l tempers makes it a logical replacement for 2024, 2014

 

and 2017 in many of the most critical applications. The T6 and T65 l tempers have fair machinability, resistance welding

 

and corrosion resistance ratings. This alloy is heavily utilized by the aircraft and ordnance industries because of its superior strength.

TYPICAL MECHANICAL PROPERTIES

 

 

 

Temper

Tensile (500" Dia Specimen)

Hardness

Shear

Fatigue*

Modulus

 

Ultimate

Yield

Elongation/4D

Bnnell 500kg 10 mm

Ultimate Shearing Strength

Endurance L1m1I - RR Moore Type

Modulus of Elast1c1ty

KSI

MPa

KSI

MPa

 

KSI

MPa

KSI

MPa

KSI x 103

Gpa

T651

83

572

73

503

11

150

48

331

23

158

10.3

71.0

T7351

73

503

63

434

13

 

44

303

23

158

10.3

710

T7651

73

503

63

434

13

 

44

303

23

158

10.3

710

W5I

 

 

 

 

 

 

 

 

 

 

 

 

*5 x IOE8 cycles ofreversed stress

 

COMPARATIVE CHARACTERISTICS

Temper

Corrosion Resistance

Cold Wokability3

Machinab山ty3

Anodize Response3

Brazeab山ty4

Weldab小ty•

 

General1

Stress2

 

 

 

 

Gas

Arc

Spot

T651

T7351

C

C

C

B

D

D

C

C

B

B

D

D

D

D

D

D

B

B

I Ratings A through E are relative ratings in decreasing order of merit, based on exposures to sodium chloride solution by intermittent spraying or immersion. Alloys

with A and B ratings can be used in industrial and seacoast atmospheres without protection. Alloys with C, D and E ratings generally should be protected at least on

faying surfaces

 

2       Stress-corrosion cracking ratings are based on service experience and laboratory tests ofspecimens exposed to the 3.5% sodium chloride alternate immersion test

A=No灿own instance offailure in service or in laboratory tests

B=No灿own instance of伽lure in service; limited failures in laboratory tests ofshort transverse specimens

C= Service failures with sustained tension stress acting in short transverse direction relative to grain structure; limited failures in laboratory tests oflong transverse specimens

D= Limited service failures with sustained longitudinal or long transverse

3       Ratings A through D for Workability (cold), A through E for Machinab小ty and A through C for Anodize Response, are relative ratings in decreasing order of merit

4       Ratings A through D for Weldab山ty and Brazeability are relative ratings defined as follows:

A= Generally weldable by all commercial procedures and methods

B= Weldable with special techniques or for specific applications that justify preliminary trials or testing to develop welding procedure and weld performance

 

C= Limited weldab山ty because ofcrack sens山vity or loss in resistance to corrosion and mechanical properties

D=No commonly used welding methods have been developed

 

Sheet Coil & Plate Alloy 7075

Technical Data

 

 

 

 

 

 

 

 

C H E M I C A L C O M P O S I T I O N L I M I T S

 

Continued Page 2 of 2

 

 

Others

Weight %

Si

Fe

Cu

Mn

Mg

Cr

Zn

Ti

Each

Total

Minimum

-

-

1.2

-

2.1

0.18

5.1

-

-

-

Maximum

0.40

0.50

2.0

0.30

2.9

0.28

6.1

0.20

0.05

0.15

 

T Y P I C A L P H Y S I C A L P R O P E R T I E S

Characteristic

 

English

Metric

Nominal Density (68 °F/20 °C)

 

0.101 lbs./in.3

2.80 Mg/m3

Melting Range

 

990 °F - 1175 °F

532 °C - 635 °C

Specific Heat (212 °F/100 °C)

 

0.23 BTU/lb. - °F

960 J/kg - °K

 

 

 

Coefficient of Thermal Expansion

 

Linear

68 °F-212 °F

20 °C-100 °C

 

13.0 micro in./in.-°F

 

23.4 micro m/m -°K

 

Volumetric 68 °F/20 °C

 

3.78 x 10-5in.3/in.3 -°F

 

68 x 10-6m3/m3 -°K

 

Thermal Conductivity (68 °F/20 °C)

T651

75 BTU/ft. - hr. - °F

130 W/m - °K

T7351

90 BTU/ft. - hr. - °F

155 W/m - °K

 

 

Electrical Conductivity (68 °F/20 °C)

 

Equal Volume

T651

33% IACS

T7351

40% IACS

 

Equal Weight

T651

105% IACS

T7351

-

 